Composé antirouille L

prix disponibles sur connexion

Le composé antirouille L est un savon de calcium performant à base d'une cire oxydée, dilué à 60 % de solides avec un solvant aliphatique ayant un point d'éclair de +72°C à +80°C. Il est formulé pour répondre aux exigences de la norme MIL-C-16173D-4 et aux spécifications associées pour la protection des cavités automobiles.

Composé cireux anticorrosion aux performances éprouvées

Rust Proof Compound L is a proven performance soap of an oxidised wax, which is cut back to 60 using a +72°C to +80°C flashpoint aliphatic solvent. formulated to meet the requirements of MIL-C-16173D-4 and associated specifications for automotive cavity protection.

Rust Proof Compound L helps prevent metal corrosion wind turbine bases, railway sleeper bolts, drill pipes aids protection of automotive under-body cavities. been softened to a grease-like material and can be by brush or by airless spray-gun, without having to product.

Avantages

  • Forme une couche étanche, non durcissante et auto-obturante
  • Pénètre dans les joints et interstices
  • Pénètre la rouille existante
  • Ne se dégrade pas et ne durcit, ne craquelle, ne s'écaille, ne glisse ni ne s'éclate

Applications

  • Partout où le fer ou l'acier est exposé à l'atmosphère, à l'intérieur comme à l'extérieur, la rouille apparaît. Rust Proof Compound L protège avant, pendant et après la transformation en pièces finies
  • Le produit peut être dilué avec un solvant hydrocarboné tel que le white-spirit

Spécifications

  • MIL-C-16173D-4
  • It has applied heat the film

Performances

  • dry conditions away from other combustible materials,
  • Meets the requirements of MIL-C-16173D-4 heat and direct sunlight. Protect from frost
  • Storage and handling | • When stored in the recommended manner, a small degree of footing of the product may occur over time,
  • How should the product be applied? | but this will not detract from the performance of the fluid in service
  • The inside of tanks must first be cleaned and dried, before a thin layer of rust proof compound is applied. | • Note: During storage a liquid brown layer can be formed
  • For restoration of old structures, the metal surface is | on top of the product. This can be easily mixed back in sand blasted and coated with a metal paint. Over this | using moderate stirring. If there is a need to make paint layer the rust proof compound L is applied. | application easier then additional dilution can be carried using an aliphatic solvent. Since Rust Proof Compound
  • L is thixotropic, during storage the product can become harder; remixing will soften the product
  • Le produit est sensible à la température de stockage. Stocké au froid, il peut durcir ; un stockage plus chaud le ramollit

Valeurs typiques

Test Test Methods Results
Rust Proof Compound L
Shelf Life: 24 months from date of filling indicated on the product label.
Appearance Visual Soft, brown, solid
Pour point, °C (pure product) ASTM D127 25
Density, 20 °C, Kg/l ASTM D1298 0.91
Active content, % — 57-63
Colour ASTM D1500 Max 7.5
Flash point, °C ASTM D92 ≥75
Salt fog resistance, hrs ASTM B117 500 at 40 µm
Solvent % ST0127 40
Solvent Type — Kero
Melting point (supplied), °C ASTM D127 25-35

Source : PDS 16 juin 2016 · Fiche technique produit

Attention : pour les informations PDS les plus récentes, rendez-vous sur https://cglapps.chevron.com/sdspds/HomePage.aspx?tab=pds