Rostschutzmasse L

Preise beim Login verfügbar

Rust Proof Compound L ist ein leistungsstarkes Kalziumseifenfett aus einem oxidierten Wachs, dessen Feststoffgehalt mit einem aliphatischen Lösemittel mit einem Flammpunkt von +72°C bis +80°C auf 60 % reduziert wurde. Es wurde entwickelt, um die Anforderungen von MIL-C-16173D-4 und den damit verbundenen Spezifikationen für den Korrosionsschutz von Fahrzeughohlräumen zu erfüllen.

Korrosionsschutz-Wachsverbindung mit bewährter Leistung

Rust Proof Compound L is a proven performance soap of an oxidised wax, which is cut back to 60 using a +72°C to +80°C flashpoint aliphatic solvent. formulated to meet the requirements of MIL-C-16173D-4 and associated specifications for automotive cavity protection.

Rust Proof Compound L helps prevent metal corrosion wind turbine bases, railway sleeper bolts, drill pipes aids protection of automotive under-body cavities. been softened to a grease-like material and can be by brush or by airless spray-gun, without having to product.

Vorteile

  • Bildet eine wasserdichte, nicht aushärtende, selbstabdichtende Schicht
  • Kriecht in Nähte und Fugen
  • Durchdringt vorhandenen Rost
  • Verwittert nicht und härtet, reißt, blättert, rutscht oder platzt nicht ab

Anwendungen

  • Überall dort, wo Eisen oder Stahl der Atmosphäre ausgesetzt ist, ob innen oder außen, entsteht Rost. Rust Proof Compound L schützt davor vor, während und nach der Verarbeitung zu Fertigteilen
  • Das Produkt kann mit einem Kohlenwasserstofflösemittel wie Testbenzin verdünnt werden

Spezifikationen

  • MIL-C-16173D-4
  • It has applied heat the film

Leistung

  • dry conditions away from other combustible materials,
  • Meets the requirements of MIL-C-16173D-4 heat and direct sunlight. Protect from frost
  • Storage and handling | • When stored in the recommended manner, a small degree of footing of the product may occur over time,
  • How should the product be applied? | but this will not detract from the performance of the fluid in service
  • The inside of tanks must first be cleaned and dried, before a thin layer of rust proof compound is applied. | • Note: During storage a liquid brown layer can be formed
  • For restoration of old structures, the metal surface is | on top of the product. This can be easily mixed back in sand blasted and coated with a metal paint. Over this | using moderate stirring. If there is a need to make paint layer the rust proof compound L is applied. | application easier then additional dilution can be carried using an aliphatic solvent. Since Rust Proof Compound
  • L is thixotropic, during storage the product can become harder; remixing will soften the product
  • Das Produkt ist temperaturempfindlich bei der Lagerung. Bei niedrigen Temperaturen kann es hart werden; wärmere Lagerung macht es wieder weich

Typische Kennwerte

Test Test Methods Results
Rust Proof Compound L
Shelf Life: 24 months from date of filling indicated on the product label.
Appearance Visual Soft, brown, solid
Pour point, °C (pure product) ASTM D127 25
Density, 20 °C, Kg/l ASTM D1298 0.91
Active content, % — 57-63
Colour ASTM D1500 Max 7.5
Flash point, °C ASTM D92 ≥75
Salt fog resistance, hrs ASTM B117 500 at 40 µm
Solvent % ST0127 40
Solvent Type — Kero
Melting point (supplied), °C ASTM D127 25-35

Quelle: PDS 16. Juni 2016 · Produktdatenblatt

Achtung: die aktuellsten PDS-Informationen finden Sie unter https://cglapps.chevron.com/sdspds/HomePage.aspx?tab=pds